Understanding the strengthening of a lateritic "geomimetic" material

Abstract : The present work aimed to investigate the interactions that control the strengthening of ''geomimetic'' materials. The raw lateritic clay used mainly contained kaolinite, goethite, quartz and hematite. The processing involved a 24 h-reaction with fulvic acid followed by neutralization with lime or with NaOH prior to the curing at 60 C for 18 days under water saturated atmosphere. The compressive strength and thermal conductivity after consolidation were respectively 0.7 MPa and 0.19Wm 1 K 1 for lime-based products, and 0.78 MPa and 0.3Wm 1 K 1 for soda-based products. The latter exhibited low durability in water. Such differences could be related to the high degradation of kaolinite particles when using NaOH, leading to the formation of sodalite, cancrinite and nontronite, which phases did not act as binder. Cementitious CAH and CSH phases were obtained when using lime. Rheological measurements performed on lime-based samples indicated that a shear-thinning behavior prevails up to the 7th day of curing. Above this period, the samples reached a determinant step whereby a solid-like behavior became predominant. The occurrence of binding precursors during the first 7 days of curing conducted to a progressive increase of the yield stress and consistency from 1 to 53 Pa and from 0.2 to 2.3 Pa s, respectively.
Type de document :
Article dans une revue
Domaine :
Liste complète des métadonnées

https://hal-unilim.archives-ouvertes.fr/hal-00955832
Contributeur : Pamela Bathias Connectez-vous pour contacter le contributeur
Soumis le : mercredi 5 mars 2014 - 13:30:21
Dernière modification le : samedi 26 mars 2022 - 04:27:30

Identifiants

Collections

Citation

Hervé Goure-Doubi, Gisèle Laure Lecomte-Nana, F. Nait-Abbou, Benoît Nait-Ali, Agnès Smith, et al.. Understanding the strengthening of a lateritic "geomimetic" material. Construction and Building Materials, 2014, 55, pp.333-340. ⟨10.1016/j.conbuildmat.2014.01.064⟩. ⟨hal-00955832⟩

Partager

Métriques

Consultations de la notice

64