Aqueous suspensions of glass silicate dielectric powders for ink-jet printing applications

M. Singlard 1 Anne Aimable 1 Martine Lejeune 1 C. Dossou-Yovo 2 Marion Poncelet 2 R. Noguéra 2 C. Modes 3 
1 SPCTS-AXE1 - Axe 1 : procédés céramiques
SPCTS - Science des Procédés Céramiques et de Traitements de Surface
Abstract : Ink-jet printing (IJP) is a rapid prototyping method which is very promising for the manufacturing of multilayer hybrid circuits. Before the formulation of inks, the first step aims to ensure the stability of dielectric powder sus-pensions with the specifications required for the IJP process in terms of solid content, particle size, rheology, and stability versus sedimentation. A commercial glass silicate powder currently used as a dielectric material was studied during an attrition milling (i) for low ceramic loading (3 vol.%) and (ii) for significant ceramic loading (20 vol.%) with different dispersants: polyelectrolytes with carboxylate groups, and sulfate groups. The milling step impact on the surface chemistry of the powder was investigated in both cases. A potassium polycarboxylate was found to be the most efficient dispersant, and the optimization of the dispersant rate was carried out through zeta potential measurements, viscosity, dispersant adsorbed rate, and sedimentation tests. An attempt of corre-lation between some of these properties is proposed. The preliminary ejection tests obtained with an ink prepared from an optimized suspension allowed to generate a wide range of drop velocity (0.7 to 4.2 m/s) and drop diameter (47 to 56 μm), which will be useful in a further step to optimize the characteristics of green ink-jet printed dielectric layers.
Type de document :
Article dans une revue
Liste complète des métadonnées

Littérature citée [32 références]  Voir  Masquer  Télécharger
Contributeur : Anne Aimable Connectez-vous pour contacter le contributeur
Soumis le : jeudi 5 février 2015 - 15:51:07
Dernière modification le : samedi 26 mars 2022 - 04:30:30




M. Singlard, Anne Aimable, Martine Lejeune, C. Dossou-Yovo, Marion Poncelet, et al.. Aqueous suspensions of glass silicate dielectric powders for ink-jet printing applications. Powder Technology, 2014, 266, pp.303-311. ⟨10.1016/j.powtec.2014.06.044⟩. ⟨hal-01108406⟩



Consultations de la notice