Experimental investigation and thermodynamic evaluation of the C–O–Zr ternary system

Abstract : The ZrCxOy oxycarbides are well-known relevant ceramic materials for ultra-high temperature applications. The intrinsic macroscopic properties of ZrCxOy being closely related to the C/O ratio, a detailed analysis of the C–O–Zr system has been undertaken experimentally in order to accurately determine the extent of the solid solution of oxygen within the oxycarbide phase at different synthesis temperatures. The obtained results were then used as diagrammatic data to extrapolate the ternary C–O–Zr phase equilibria diagram by the CALPHAD method, providing a predictive tool for the oxycarbide synthesis. The model proposed in the temperature range 1650–2000 °C is in fair agreement with results obtained in the literature. The chemical determination of the relative ratio between light elements (oxygen (O) and carbon (C)) being a difficult issue for most of the general applications, an accurate determination of the cell parameters of the different oxycarbide compositions has been performed to propose an abacus reporting the evolution of the cell parameter against the C/O amount. The chemical composition of the oxycarbide is shown to be determined with an accuracy better that a few percent. It is also shown that the evolution of the cell parameter is not linear, indicative of a possible change of the ionocovalent character of the chemical bonds with the composition of ZrCxOy.
Liste complète des métadonnées

Littérature citée [29 références]  Voir  Masquer  Télécharger
Contributeur : Olivier RAPAUD Connectez-vous pour contacter le contributeur
Soumis le : mercredi 9 novembre 2016 - 16:49:36
Dernière modification le : samedi 26 mars 2022 - 04:29:53



Florian Réjasse, Olivier Rapaud, Gilles Trolliard, Olivier Masson, Alexandre Maitre. Experimental investigation and thermodynamic evaluation of the C–O–Zr ternary system. RSC Advances, 2016, 6, pp.100122-100135. ⟨10.1039/C6RA21967E⟩. ⟨hal-01386236⟩



Consultations de la notice