Influence of sintering temperature on the microstructural and mechanical properties of cordierite synthesized from andalusite and talc

A. Benhammou; Y. El Hafiane; A. Abourriche; Y. Abouliatim; L. Nibou; A. Yaacoubi; Nicolas Tessier-Doyen; Agnès Smith; B. Tanouti

Influence of sintering temperature on the microstructural and mechanical properties of cordierite synthesized from andalusite and talc

A. Benhammou ¹ Y. El Hafiane ² A. Abourriche ² Y. Abouliatim ² L. Nibou ² A. Yaacoubi ³ Nicolas Tessier-Doyen ⁴ Agnès Smith ⁴ B. Tanouti ⁵

1 LMPEQ - Laboratoire Matériaux Procédés Environnement Qualité

2 ENSA - Ecole Nationale des Sciences Appliquées [Safi]

3 FSSM - Faculté des Sciences SEMLALIA

4 SPCTS - Science des Procédés Céramiques et de Traitements de Surface

5 Laboratoire de Chimie du Solide Mineral

Abstract : Cordierite-based ceramic has been synthesized by solid state process from andalusite and talc mixture sintered at 1300 and 1350 °C for 2 h. The phase, microstructural and thermal characterizations of the samples were investigated using X-ray diffraction (XRD), scanning electron microscope (SEM), dilatometric and thermal analysis (TG/DTA). Brazilian and three-point bending tests were performed to evaluate the mechanical properties. XRD results showed a significant improvement in the cordierite formation at 1350 °C, whereas the sintering at 1300 °C was insufficient. The SEM observation showed that the sample sintered at 1350 °C was relatively dense. As a result of this densification, the flexural and tensile strengths at 1300 °C (15.4±1.2 and 12.2±1.9 MPa, respectively) were significantly enhanced with increasing temperature to 1350 °C (32±4.2 and 18.3±3.6 MPa, respectively).

Keywords : Cordierite Talc Andalusite Sintering Mechanical properties

Type de document :

Article dans une revue

Domaine :

Chimie / Matériaux

Sciences de l'ingénieur [physics] / Matériaux

Liste complète des métadonnées

https://hal-unilim.archives-ouvertes.fr/hal-01875322
Contributeur : Beatrice Derory <>
Soumis le : lundi 17 septembre 2018 - 11:15:00
Dernière modification le : vendredi 9 août 2019 - 15:18:07

Influence of sintering temperature on the microstructural and mechanical properties of cordierite synthesized from andalusite and talc

Identifiants

Collections

Citation

Exporter

Métriques

76

Influence of sintering temperature on the microstructural and mechanical properties of cordierite synthesized from andalusite and talc

Identifiants

Collections

Citation

Exporter

Partager

Métriques

76