A comprehensive study of the glass/translucent anti-glass/transparent ceramic structural ordering in the Bi2O3Nb2O5–TeO2 system

Morgane Dolhen (1) , Mathieu Allix (2) , Vincent Sarou-Kanian (2) , Franck Fayon (2) , Cécile Genevois (2) , Sébastien Chenu (1) , Pierre-Eugène Coulon (3) , Maggy Dutreilh-Colas (1) , Julie Cornette (4) , Jean-René Duclere (1) , François Brisset (5) , Olivier Masson (1) , Philippe Thomas (1) , Gaëlle Delaizir (1)

1 IRCER-AXE3 - IRCER - Axe 3 : organisation structurale multiéchelle des matériaux
2 CEMHTI - Conditions Extrêmes et Matériaux : Haute Température et Irradiation
3 CEMES - Centre d'élaboration de matériaux et d'études structurales
4 IRCER - Institut de Recherche sur les CERamiques
5 ICMMO - Institut de Chimie Moléculaire et des Matériaux d'Orsay

The full and congruent crystallization of the Bi0.8Nb0.8Te2.4O8 (BNT) glass leads to perfectly transparent ceramic in both the visible and near infrared ranges. While heating the parent glass, an intermediate structural regime order-called anti-glass-that shows chemical inhomogeneity at the nanometer scale and with a long-range cationic ordering while retaining a strong local anionic disorder is observed. Here, we report on the crystallization sequence starting from the Bi0.8Nb0.8Te2.4O8 glass system and show that an intermediate Bi0.8Nb0.8Te2.4O8 anti-glass phase (polymorph 1) is first formed, before transforming into a more ordered and ceramic material (polymorph 2). In particular, we provide a comprehensive structural study of the crossover between glass and its crystalline counterpart through intermediate steps. Similarities and differences between the structures, microstructures of Bi0.8Nb0.8Te2.4O8 glass, anti-glass and ceramic materials of identical composition are investigated in details at different length scales 2 by X-ray and neutron powder diffraction, SEM-EBSD, TEM, NMR and Raman spectroscopy. The optical properties of the anti-glass and ceramic are discussed in correlation with the structure and microstructure observations. This study paves the way for understanding the complex mechanisms at the origin of the full and congruent crystallization from the parent glass.

Domaines: Matériaux; Chimie inorganique

Morgane Dolhen, Mathieu Allix, Vincent Sarou-Kanian, Franck Fayon, Cécile Genevois, et al.. A comprehensive study of the glass/translucent anti-glass/transparent ceramic structural ordering in the Bi2O3Nb2O5–TeO2 system. Acta Materialia, 2020, 189, pp.73-84. ⟨10.1016/j.actamat.2020.02.062⟩. ⟨hal-02551064⟩