Thermal, optical and structural properties of glasses within the TeO2TiO2ZnO system

Abstract : A glass-forming domain was evidenced and studied within the TeO2single bondTiO2single bondZnO system. Density, glass transition temperature (Tg) and onset crystallization temperature (T0) were measured and interpreted as a function of the zinc oxide mole fraction for relevant glasses. It was concluded that the zinc oxide favors the thermal stability of glasses. On the other hand, the impact of TiO2 addition is even more pronounced on the enhancement of the thermal stability. The optical transmission was recorded for series of glasses in the UV–Visible–NIR range. Refractive index and optical band gap were extracted from these measurements and studied as a function of the ZnO content. Linear refractive indices and optical band gap were found to decrease and increase respectively, with increasing ZnO content. The third-order non-linear susceptibility Re (χ3), measured for two series of glasses (TiO2 content was fixed either to 5 or 10 mol%), was found to progressively decrease when the ZnO concentration increases. The impact of ZnO modifier on the glass structure was discussed based on Raman spectroscopy data. We evidenced that TiO2 does not change drastically the glass network, whereas ZnO leads in a first step to the breaking of the Tesingle bondOsingle bondTe bridges, inducing network depolymerization. A further addition in ZnO leads to the formation of new Tesingle bondOsingle bondZn and Znsingle bondOsingle bondZn linkages.
Type de document :
Article dans une revue
Domaine :
Liste complète des métadonnées
Contributeur : Claire Douady Connectez-vous pour contacter le contributeur
Soumis le : mercredi 10 décembre 2014 - 11:22:54
Dernière modification le : samedi 26 mars 2022 - 04:27:39




Nabila Ghribi, Maggy Colas, Jean-René Duclere, Philippe Thomas, T. Hayakawa, et al.. Thermal, optical and structural properties of glasses within the TeO2TiO2ZnO system. Journal of Alloys and Compounds, 2015, 622, pp.333-340. ⟨10.1016/j.jallcom.2014.10.063⟩. ⟨hal-01093138⟩



Consultations de la notice