Cationic Order–Disorder in Double Scheelite Type Oxides: the Case Study of Fergusonite La 2 SiMoO 8

Abstract : Up to now, the possible occurrence of a cationic ordering on the tetrahedral sublattices of stoichiometric double scheelite-type oxides was not settled, with somewhat contradictory X-ray diffraction and optical measurements [Blasse, G. J. Inorg. Nucl. Chem. 1968, 30, 2091]. Using two different synthesis routes, both ordered and disordered forms of fergusonite La2SiMoO8 were prepared. The crystal structure of the ordered form was determined using powder X-ray and neutron diffraction, which clearly evidence a tridimensional ordering between [SiO4] and [MoO4] tetrahedra. The crystal chemistry of ordered double sheelite-type LaIII2(SiIVO4)(MoVIO4) can be seen as an intermediate between those of simple regular scheelite or fergusonite LnIII(NbVO4) and of ordered triple scheelite BiIII3(FeIIIO4)(MoVIO4)2. The structure of the disordered La2SiMoO8 phase was analyzed using powder X-ray diffraction. A few small and larger diffraction peaks or bumps are observed in addition to the sharper peaks of a simple fergusonite cell. DIFFaX and FAULTS programs helped showing that these faint peaks originate from stacking faults between 2D ordered layers. The intermediate 2D–3D nature of SiO4/MoO4 ordering in seemingly disordered compounds might explain the previous discrepancy between optical and X-ray diffraction measurements.
Type de document :
Article dans une revue
Liste complète des métadonnées

https://hal-unilim.archives-ouvertes.fr/hal-03249481
Contributeur : BEATRICE DERORY Connectez-vous pour contacter le contributeur
Soumis le : jeudi 9 décembre 2021 - 18:47:53
Dernière modification le : mercredi 8 juin 2022 - 16:14:04

Fichier

Manuscript La2MoSiO8 Scheelite...
Fichiers produits par l'(les) auteur(s)

Identifiants

Citation

Philippe Lacorre, Antoine Pautonnier, Sandrine Coste, Maud Barré, Emilie Béchade, et al.. Cationic Order–Disorder in Double Scheelite Type Oxides: the Case Study of Fergusonite La 2 SiMoO 8. Inorganic Chemistry, American Chemical Society, 2021, 60 (4), pp.2623-2633. ⟨10.1021/acs.inorgchem.0c03491⟩. ⟨hal-03249481⟩

Partager

Métriques

Consultations de la notice

57

Téléchargements de fichiers

36